Glass fiber reinforced 15% modified PA66 for chain processing with stable mechanical properties
Click:
PA66 plus glass fiber 15% reinforced modification
Features:
Excellent appearance, stable mechanical properties
Glass fiber reinforced 15% modified PA66 for chain processing Physical property table:
Testing Standards | Data | Unit | |
Density | ASTM D792 | 1.23 | g/cm3 |
Shrinkage | ASTM D955 | 1.2-1.4 | In./in |
Tensile strength | ASTM D638 | 135 | MPa |
Elongation at break | ASTM D638 | 9 | % |
Flexural strength | ASTM D790 | 210/170 | MPa |
Flexural modulus | ASTM D790 | 6000/4500 | GPa |
Notched Impact Strength | ASTM D256 | 14 | KJ/m2 |
Heat distortion temperature | ASTM D648 | 235 | ℃(1.8MPa) |
Flame retardant performance | UL94 | HB |