PA6+30% glass fiber reinforced nylon modified material
Click:
PA6 glass fiber reinforced 30%,
Excellent mechanical properties,
excellent appearance,
Dimensionally stable and high strength.
PA6+30% glass fiber reinforced modified material property table:
Testing Standards | Data | Unit | |
Density | ASTM D792 | 1.36 | g/cm3 |
Shrinkage | ASTM D955 | 0.4-0.6 | In./in |
Tensile Strength | ASTM D638 | 163 | MPa |
Elongation at break | ASTM D638 | % | |
Flexural strength | ASTM D790 | 230 | MPa |
Flexural modulus | ASTM D790 | 8000 | GPa |
Notched Impact Strength | ASTM D256 | 14 | KJ/m2 |
Heat distortion temperature | ASTM D648 | 210 | ℃(1.8MPa) |
Flame retardant performance | UL94 | HB |